WHAT CAUSE DEFECTS IN BRICK MASONRY AND ITS REMEDIES?




SOURCES OF DEFECTS IN BRICK MASONRY
There are 4 primary reasons that cause defects in brick masonry work. These are as follows.

Sulphate Attack
Crystallization of Salts from Bricks
Corrosion of Embedded Iron or Steel
Shrinkage on Drying
1. SULPHATE ATTACK

The common forms of defects due to sulphate attack are

Chipping and spalling of bricks and
Formation of cracks in joints and rendering
These types of defects happens when sulphate salts present in brick work

react with alumina of cement in case of cement mortar or
react with hydraulic lime in case of lime mortar
This reaction causes increase in the volume of mortar and consequently leads to cracks, chipping and spalling of brick work.

‎These defects are commonly found in following situation;

exposed boundary wall
parapet wall
manhole and retaining walls (where they come in contact with moisture)
This type of defects can be prevented by adopting suitable construction detail and good quality materials that prohibits entry of moisture into the body of brick work.

2. CRYSTALLIZATION OF SALTS FROM BRICKS

Defect formed due to crystallisations of salts from brick are known as efflorescence.
‎
Presence of excessive soluble salts in the brick is the primary cause of this type of defect. When these brick come in contact with water, the soluble salts present therein gets dissolved and comes to surface in the form of whitish powder.‎

Due to this defect the wall looks dull and losses it aesthetic look.

The only way to cure this defect is by repeatedly brushing and washing the wall surface.

3. CORROSION OF EMBEDDED IRON OR STEEL

Formation of cracks in brick work falls in this category.

Dampness in building causes corrosion of embedded iron or steel. Corrosion of steel results in increase in the volume of metal and thereby leads to crack in brick work.

The defect due to corrosion of steel or iron can be prevented by encasing the reinforcement in thick and impermeable cement mortar and providing a cover of 15 to 25 mm around the embedded member.

4. SHRINKAGE ON DRYING

Formation of cracks in masonry joints is one form of defect due to shrinkage.

As brick are porous material it has tendency to absorb water. When it absorbs water it swells and when this absorbed water evaporates brick starts to shrink. This shrinkage of brick creates cracks in brick masonry joints.‎

The formation and type of crack occurs is dependent upon type of mortar used in brick masonry. Where lean mortar is used in brick masonry crack get distributed over large number of joints and where thick mortar is used cracks are few but wider.

Shrinkage cracks do not affect the structural strength of brick work and it can be easily prevented

by using good quality of brick and mortar
by protecting masonry from moisture‎

Comments

Post a Comment

Popular posts from this blog

How To Calculate or Estimate Long-span Aluminium Roofing Sheets.

Image
Aluminium roofing sheets, they come in rolls of average of 600mm to 1300mm depends on the manufacture and specifications. As stated in previous articles, the aluminium sheets comes in rolls at the factory just like toilet rolls but with different widths and thickness based on specifications. Calculating the roof required could be done by calculating the surface area in square meters of the area covered by the aluminium and for some companies it could be calculated in meter lengths ,knowing the width which is 600mm above as constant. For a simple gable roof as shown in pic 1 with length of 25.2m. First you must know the height of roof from the section. For this sample we are taken the eight to be 3meters (10 feet)to know the length of leaf “x” or “y” Remember the pythagoras theorem x2=32 +6.12 x=6.8m Hence the area of roof is (6.8 i.e x)+6.8 i.e y) multiply by length 25.2m=342.72m2 If the width of the roof comes in 600mm or 0.6m, the length of the roof ...
Read more

Post Tension Slab – Advantages and Disadvantages of Post Tension Slab

Image
Post Tension Slab Although concrete is a strong material for construction, it is not resistant to breakdown especially where longer concrete slabs are required like in a bridge or a length of a beam. For this, the concrete slab is tensioned with a process called pre-stressing and the slab of concrete which comes out after this process is known as post tension slab. This slab is much stronger as well as more durable than the normal concrete slabs. In today’s world, where the modern engineering is finding new ways to build longer, more efficient and stronger structures, post tension slab becomes one of their chief requirements. There are many advantages and disadvantages of post tensioned slabs which we will discuss in this post. Advantages of Post Tension Slab Post tension slabs are advantageous in many ways. Some of the major benefits of post tension slabs are as follows. 1. Reduced cost: Post tension slabs are excellent ways to construct stronger structures at an affordable...
Read more

How to install POP (plaster of paris) ceilling

Image
Plaster of Paris is regarded as any type of plaster containing calcined gypsum (calcium sulfate dihydrate), sand and water. When these ingredients are combined, they result in the formation of a tough, dry product; however, plaster of Paris can be sanded to achieve a variety of looks. By following some basic guidelines, you can use plaster of Paris to mend cracks, fix dents,for ceiling, in walls and even to create artworks. However in this case our focus is on ceiling. POP popularly called plaster of Paris is used for a lot of purposes because it can easily be formed to any shape and it hardens quickly and is easy to operate. To do a pop ceiling in your home, getting it done is in two ways, you can buy the materials yourself which include pop cement , yarn(sponge-like material) etc then pay the installer based on per square meter of area of coverage, or you can give it out totally as a contract. But these are the basic steps in getting pop ceiling cast-on-site done. Get cemen...
Read more